316 stainless steel, 06cr17ni12mo2 (old 0Cr17Ni12Mo2, American Standard s31608) has excellent corrosion resistance, atmospheric corrosion resistance and high temperature strength due to the addition of Mo, which can be used under cool conditions;
- Fast Delievery
- Quality Assurance
- 24/7 Customer Service
Product Introduction
316 stainless steel, 06cr17ni12mo2 (old 0Cr17Ni12Mo2, American Standard s31608) has excellent corrosion resistance, atmospheric corrosion resistance and high temperature strength due to the addition of Mo, which can be used under cool conditions; Excellent work hardening (non-magnetic). Seawater equipment, chemical, dye, papermaking, oxalic acid, fertilizer and other production equipment; Photography, food industry, coastal facilities, ropes, CD rods, bolts, nuts, etc.
chemical composition
Chemical composition/% | ||||||||||
Grade | C | Si | Mn | P | S | Ni | Cr | Mo | N | Other |
316 | ≤0.08 | ≤1 | ≤2 | ≤0.045 | ≤0.030 | 10.0~14.0 | 16.0~18.0 | 2.00-3.00 | — | |
Mechanical Property
Brand | heat treatment | yield strength σ0.2/Mpa | tensile strength σb/Mpa | Elongation δ5/% | HBS | HRB | HV |
316 | 1010~1120 fast cooling | ≥205 | ≥520 | ≥40 | ≤187 | ≤90 | ≤200 |
Corrosion resistance
The corrosion resistance is better than 304 stainless steel, which has good corrosion resistance in the production of pulp and paper. Moreover, 316 stainless steel is also resistant to the corrosion of ocean and aggressive industrial atmosphere.
Heat resistance
316 stainless steel (06cr17ni12mo2) has good oxidation resistance in intermittent use below 871 ° C (1600 ° f) and continuous use above 927 ° C (1700 ° f). In the range of 427 ° c-857 ° C (800 ° f-1575 ° f), it is better not to use 316 stainless steel continuously, but when using 316 stainless steel continuously outside this temperature range, the stainless steel has good heat resistance. The carbide precipitation resistance of 316L stainless steel is better than that of 316 stainless steel, and the above temperature range can be used.
Heat treatment
Annealing in the temperature range of 1850-2050 ° F, then rapid annealing, and then rapid cooling. 316 stainless steel cannot be hardened by heat treatment.
Welding
316 steel material is austenitic stainless steel. 316 stainless steel is the most widely used food grade stainless steel after 304 stainless steel. 316 stainless steel has a wider range of applications and has the characteristics of high temperature resistance and corrosion resistance. Because Mo element is added to 316 stainless steel, its physical and chemical properties are more stable, and it can still be used normally in high temperature environments. It can withstand high temperatures of up to 1300 degrees. In addition, the strength of 316 stainless steel is also greatly enhanced. At present, it is mainly used in large equipment exchangers and exterior materials for coastal buildings.
Typical use
Pulp and paper equipment heat exchangers, dyeing equipment, film processing equipment, pipelines, materials for the exterior of buildings in coastal areas.
In 2013, it should also be used in the field of solenoid valves, mainly for shells, clamps, spheres, valve bodies, valve seats, nuts, valve stems, etc.